| Kristalline Phase | Q-Al2O3 |
|---|---|
| Chemische Formel | Al2o3 |
| Partikelgröße | 1.6 bis 1.8 mm |
| Cao-Gehalt | ≤ 0,05% |
| Feuchtigkeitsgehalt | ≤ 1% |
| Kristalline Phase | Q-Al2O3 |
|---|---|
| Feuchtigkeitsgehalt | ≤ 1% |
| Cao-Gehalt | ≤ 0,05% |
| MgO-Gehalt | ≤ 0,05% |
| Fläche | 100 bis 110 M2/g |
| Pore Volume | 0.6-0.8 Cm3/g |
|---|---|
| Surface Area | 100-110 M2/g |
| Thermal Stability | Up To 1200℃ |
| Fe2O3 Content | ≤0.02% |
| Chemical Formula | Al2O3 |
| Sio2 Content | ≤0.05% |
|---|---|
| Thermal Stability | Up To 1200℃ |
| Mgo Content | ≤0.05% |
| Bulk Density | 0.6-0.65 G/cm3 |
| Pore Volume | 0.6-0.8 Cm3/g |
| Particle Size | 1.6-1.8mm |
|---|---|
| Chemical Formula | Al2O3 |
| Crystalline Phase | Q-Al2O3 |
| Bulk Density | 0.6-0.65 G/cm3 |
| Na2O Content | ≤0.2% |
| Thermal Stability | Up To 1200℃ |
|---|---|
| Na2O Content | ≤0.2% |
| Appearance | White Powder |
| MgO-Gehalt | ≤ 0,05% |
| Cao Content | ≤0.05% |
| Pore Volume | 0.6-0.8 Cm3/g |
|---|---|
| Na2O Content | ≤0.2% |
| Surface Area | 100-110 M2/g |
| Crystalline Phase | Q-Al2O3 |
| Moisture Content | ≤1% |
| Aussehen | Weißes Pulver |
|---|---|
| Na2O-Inhalt | ≤ 0,2% |
| Massendichte | 00,6-0,65 G/cm3 |
| Chemische Formel | Al2O3 |
| MgO-Gehalt | ≤ 0,05% |
| Aussehen | Weißes Pulver |
|---|---|
| Wärmestabilität | Bis zu 1200℃ |
| Cao-Gehalt | ≤ 0,05% |
| Partikelgröße | 1.6 bis 1.8 mm |
| Fläche | 100 bis 110 M2/g |
| Fläche | 100 bis 110 M2/g |
|---|---|
| Aussehen | Weißes Pulver |
| Inhalt Fe2O3 | ≤0,02 % |
| Feuchtigkeitsgehalt | ≤1% |
| Massendichte | 00,6-0,65 G/cm3 |